Submerged arc welding flux
Description:
1.the welding flux is fluorine alkali type sintered flux.
2. Grain size: 10-60(2.0-0.3mm) meshes.
3. Performance:
A. Easy to deslag.
B. Sulfur removal, phosphor removal and anti-rust.
C. Fine appearance of weld (even in the narrow gap of deep slope entrance).
D. Metal welding seam: Good plastic toughness, low hydrogen content diffusion and fine properties of cold, heat and crack resistance.
Usage:
1. welding flux is For low carbon, low alloy and pipeline steel.
2. welding flux is For thick wall structures of different high-tensile steels.
Cautions:
1. The oil contamination, moisture, iron rust and other foreign substances must beremoved from the welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 250-300°C for more than 2 hours
Before usage.
Chemical Compositions: (%)
welding flux Basicity B/w=1.6--1.8
Mechanial performance of the deposited metal:
Description:
1.the welding flux is fluorine alkali type sintered flux.
2. Grain size: 10-60(2.0-0.3mm) meshes.
3. Performance:
A. Easy to deslag.
B. Sulfur removal, phosphor removal and anti-rust.
C. Fine appearance of weld (even in the narrow gap of deep slope entrance).
D. Metal welding seam: Good plastic toughness, low hydrogen content diffusion and fine properties of cold, heat and crack resistance.
Usage:
1. welding flux is For low carbon, low alloy and pipeline steel.
2. welding flux is For thick wall structures of different high-tensile steels.
Cautions:
1. The oil contamination, moisture, iron rust and other foreign substances must beremoved from the welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 250-300°C for more than 2 hours
Before usage.
Chemical Compositions: (%)
Al2O3+MnO | CaO+MGO | SiO2+TiO2 | CaF2 | S, P |
25~30 | 25~30 | 15~20 | 15~20 | ≤ 0.05 |
welding flux Basicity B/w=1.6--1.8
Mechanial performance of the deposited metal:
Wires | Standard Models |
S (Mpa) |
B (Mpa) |
Akv (J) |
Δ5 |
HO8A HO8MnA HO8Mn2MoA |
F4A2-HO8A F5A4-HO8MnA F7021-HO8Mn2MoA |
≥340 ≥410 ≥500 |
≥420 ≥490 ≥600 |
≥27(-20ºC) ≥27(-40ºC) ≥27(-20ºC) |
≥22% ≥22% ≥17% |